Everything about Stoneware totally explained
Stoneware is a category of clay and a type of
ceramic distinguished primarily by its firing and maturation
temperature (from about 1200
°C to 1315 °C). In essence, it's
man-made
stone. One widely recognized definition is from the
Combined Nomenclature of the European Communities which states, "Stoneware, which, though dense, impermeable and hard enough to resist scratching by a steel point, differs from porcelain because it's more opaque, and normally only partially vitrified. It may be vitreous or semi-vitreous. It is usually coloured grey or brownish because of impurities in the clay used for its manufacture, and is normally glazed".
In contrast,
earthenware is fired at lower temperatures and isn't impervious to liquids.
Porcelain, which some consider to be a type of stoneware, is distinguished as being whiter than stoneware and always vitreous.
Kaolin, or China Clay, has a lower content of impurities than many other clays. It is also fired to a
vitreous state, transforming the constituent
silica into
glass. Some porcelain bodies are
translucent after firing. Firing a piece of pottery to too high a temperature will result in warping or melting. Vitreous clay bodies can be made at different temperatures ranges, but they're typically fired in the stoneware/porcelain range. Fired stoneware absorbs up to 5% water, porcelain 0%, and earthenware up to 10%. Earthenware, when moist, is typically not freeze resistant.
Clay refers to group of
minerals that generally exhibit
plasticity when mixed with water, and which chemically primarily consist of
alumina and silica. Potters refer to combinations of clays mixed with other materials as clay bodies. Different kinds of clay bodies are created by mixing additives, such as
feldspar,
grog,
quartz,
flint, many other minerals are used and these can include
spodumene,
wollastonite to modify clays. Clay bodies can thereby be formulated to fire at a range of temperatures. Darker clays often contain iron and other metal oxide impurities. The clay used for porcelain and white stoneware clay bodies contain very little of these impurities.
Glaze may be applied to stoneware pottery before a second firing at a different temperature, or a glaze may be applied before a single, raw firing.
Salt-glazed stoneware became the dominant houseware of nineteenth century America.
Further Information
Get more info on 'Stoneware'.
|
External Link Exchanges
Do you know how hard it is to get a link from a large encyclopaedia? Well we're different and will prove it. To get a link from us just add the following HTML to your site on a relevant page:
<a href="http://stoneware.totallyexplained.com">Stoneware Totally Explained</a>
Then simply click through this link from your web page. Our crawlers will verify your link, extract the title of your web page and instantly add a link back to it. If you like you can remove the words Totally Explained and embed the link in article text.
As long as your link remains in place, we'll keep our link to you right here. Please play fair - our crawlers are watching. Your site must be closely related to this one's topic. Any kind of spamming, dubious practises or removing the link will result in your link from us being dropped and, potentially, your whole site being banned. |